KERA® C
Chemical composition*
| Co | Cr | W | Nb | V | Mo | Si | Fe | others |
| 60 | 24,5 | 9 | 2 | 2 | 1,1 | 0,9 | 0,15 | < 0,1 |
*Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.
Cobalt based dental casting bonding alloy,
type 5
KERA®C - CoCr alloy for universal requirements
Indications
- Ceramic veneered crowns and bridges
- Telescopic crowns
- Combinated restorations
- Attachments
Typical values*
| yield strength RP 0,2 % (MPa) | 575 |
| elongation (%) | 4,25 |
| young's modul (GPa) | 170 |
| tensile strength (MPa) | 750 |
| density (g/cm3) | 8,4 |
| casting temperature (°C) | 1485 |
| CTE (25 – 500°C) | 14,1 |
| hardness (HV 10/30) | 350 |
| dimension, diameter and length (mm) | Ø 8 x 15 |
| type DIN EN ISO 22674 | ≥ type 5 as delivered |
Chemical composition*
| Co | Cr | W | Nb | V | Mo | Si | Fe | others |
| 60 | 24,5 | 9 | 2 | 2 | 1,1 | 0,9 | 0,15 | < 0,1 |
*Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.