Weight | 5 kg |
---|---|
Yield strength (MPa) |
770 |
Elongation (%) |
8 |
Young’s modul (GPa) |
200 |
Tensile modulus (MPa) |
1021 |
Density (g/cm³) |
8.55 |
CTE (25 - 500°C) (10¯⁶K¯¹) |
14.2 |
Hardness (HV 10/30) |
352 |
Grain size |
10 – 45 µm |
Packaging |
5 kg Container |
KERA®S-Powder
CoCrW-Powder for additive manufacturing of dental restorations for the laser-melting process, Type 5.
- Clinical proven composition on the base of Kera®-Disc
- Excellent material properties for many indications
- Approved for the most common 3D-Laser-Melting Systems
- Suitable for all high fusing veneering ceramics
Indications:
- Crowns and bridges
- Partial dentures
- Implant supported restorations
- Secondary and Tertiary frames
995.00 € 845.75 € Without VAT
169.15 €/kg
Discount per Quantity
Quantity | 1 -9 | 10 -19 | 20 + |
---|---|---|---|
Price | 845.75 € | 845.75 € | 845.75 € |
Price per kg | 845.75 € | 845.75 € | 845.75 € |
SKU:
1004000-PK
Categories: 3D PRODUCTS, SPECIAL OFFERS
Additional information
Related products
KERA®MODEL 3D
Special resin for 3D printing for the production of high-precision dental models.
- Finest detail
- Dimensionally stable
- Heat resistant
- High strength
- Short printing times
- Crown and bridge models
- Aligner models
- Orthodontic models
- Implant models
KERA®CAST 3D
Residue-free burnable special resin for 3D printing. For further processing in the 3D+CAST process.
- Low viscosity for perfect detail precision
- Short printing times
- Burns without residues for smooth casting results
- Harmonised 3D+CAST system for safe and perfect casting results with the Kera®Vest 3D investment material and the Eisenbacher casting alloys
- Crowns and Bridges
- Partial dentures
KERA®Ti5-DISC
72.00 € – 128.00 € Without VAT
NPM Titanium-Aluminium-Vanadium based dental alloy for milling, grade 5 ELI (Medical Grade 23)
- Clinical approved titanium alloy with high strength
- Very good milling properties
- Suitable for veneering with Ti-ceramics
- Crowns and bridges
- One piece abutments
- Implant retained suprastructures